Synthesis of the SrFeO<SUB>2.5</SUB> and BaFeO<SUB>3-x</SUB> perovskites by thermal decomposition of SrNh<SUB>4</SUB>[Fe(Cn)<SUB>6</SUB>] 3H<SUB>2</SUB>O and BaNh<SUB>4</SUB>[Fe(Cn)<SUB>6</SUB>]

Abstract

In the present work the synthesis, physicochemical characterization and thermoanalytical results of SrNh<SUB>4</SUB>[Fe(Cn)<SUB>6</SUB>] 3H<SUB>2</SUB>Oy BaNh<SUB>4</SUB>[Fe(Cn)<SUB>6</SUB>] are described. The thermal decompositions in oxygen atmosphere for both salts are carried out in the stages that lead to the formation of mixed oxides, i. e., SrFeO2.5 and BaFeO3-x at 1173 K. Barium carbonate is also obtained in the residue in the case of the decomposition of the barium complex. The total weight loss are 49,95% and 35,45 % for the strontium and barium salts, respectively. A decomposition mechanism is suggested for the pyrolisis processes from the data provided by IR spectroscopy, X-ray powder diffraction and chemical analysis. The specific surface area of the obtained oxides is also determined in order to evaluate its eventual catalytic activity.

En el presente trabajo se describe la síntesis, caracterización físicoquimica y resultados termoanalíticos de SrNh<SUB>4</SUB>[Fe(Cn)<SUB>6</SUB>] 3H<SUB>2</SUB>O y BaNh<SUB>4</SUB>[Fe(Cn)<SUB>6</SUB>]. Las descomposiciones térmicas en atmósfera de oxígeno para ambas sales mixtas se lleva a cabo en tres etapas que conducen a la formación de los óxidos mixtos SrFeO2.5 y BaFeO3-x a 1173 K. En el caso de la descomposición del complejo de bario se obtiene también carbonato de bario en el residuo. Las pérdidas de peso totales son del 49,95 % y del 35,45 % para la sal de estroncio y bario, respectivamente. Se propone un mecanismo de descomposición para los procesos de pirólisis a partir de la información provista por espectroscopía IR, difracción de rayos X de polvos y análisis químico. También se determina el área superficial específica de los óxidos obtenidos para evaluar su eventual actividad catalítica.