Abstract

Hysteresis loops at room temperature have been observed and investigated in nanostructures and nanoparticles ofCupric Oxide (CuO) with same average grain size. Morphological and structural properties of the studied sampleswere characterized using x-ray diffraction (XRD) and scanning electron microscopy (SEM). Energy-dispersive X-rayspectroscopy (EDS) was employed to analyze the possible presence of impurities. Mean crystallite diameter sizeswere determined using Rietveld refinement analysis of the diffraction patterns. The results suggest that hysteresisloops morphology depend on the process to obtain each sample, which not only affect grain size, but also mayinduce anisotropic forms and residual microstrains.

Lazos de histéresis a temperatura ambiente han sido observados y estudiados en nanoestructuras y nanopartículas de óxido cúprico (CuO) con el mismo tamaño promedio de cristalito. Las propiedades morfológicas y estructurales de las muestras fueron caracterizadas usando difracción de rayos X y microscopía electrónica de barrido (SEM). La presencia de impurezas ha sido descartada a partir de resultados de espectrometría de dispersión de energía de rayos X (EDS). El tamaño promedio de los cristalitos ha sido determinado usando el método de refinamiento de Rietveld de los patrones de difracción. Los resultados sugieren que las características de los lazos de histéresis dependen del proceso de obtención de las muestras, el que no sólo influye en el tamaño de grano sino también puede inducir formas y micro tensiones residuales anisotrópicas.